Flowability and Moldability of Zirconia Micro-Part Via Micro-Powder Injection Molding

The micro-powder injection moulding process is a favourable process to produce micro-sized components of zirconia. The aim of this study is to study the flowability of zirconia feedstock and to ensure the moldability of micro-sized zirconia parts without any defects. To obtain the critical powder volume percentage (CPVP), zirconia was deposited inside a Brabender mixer while oil was added gradually with an interval of three minutes. The value of 2,3 and 4 vol.% less than CPVP was mixed with palm stearin and low-density polyethylene (LDPE) binders to produce three feedstocks and run through a rheometer to test the flowability of each feedstock. The feedstock with the best flowability characteristic was then subjected to micro-powder injection moulding process through trial and error to achieve the optimum parameters for micro-sized zirconia part without any defects. The CPVP of zirconia achieved for this study was 49.92 vol.% in which the optimal loadings of 46 vol.%, 47 vol.% and 48 vol.% feedstocks were analysed using the rheometer. The results show that 46 vol.% feedstock was most suitable for producing zirconia micro-part without any defects compared to other powder loadings due