Mechanical Behaviour Slenderness Ratio of 13 Solid Wall Panels Under Uniformly Distributed Load

Recently, there has been a lot of research in the concrete industry on a sustainable approach using concrete waste as a substitute for natural aggregates. The reason for this is that the quantities of construction and demolition waste generated today pose a significant threat to the environment but can be used as a useful concrete material in the construction industry. The aim of this study is therefore to investigate the mechanical behaviour of solid concrete wall panels containing recycled concrete aggregates as a partial substitute for natural fine aggregates. Mortar cubes and wall panels with dimensions of 50 mm x 50 mm x 50 mm and 1000 mm x 300 mm x 75 mm, respectively, were produced. The wall panels were made from a 1:4 concrete mix consisting of 50% recycled concrete and 5% perlite (to reduce the weight of the concrete, and improve its workability), and 1% superplastizer, while the control wall was made with 100% natural fines. The wall panels were subjected to a compression test under uniformly distributed load. The cube samples were tested at 28 days of age. Mortar cubes with RCA achieved the highest compressive strength of 16.27 MPa compared to the control sample. The con