Objectives: This study investigated the effects of two surface treatment protocols on the shear bond strength, bond durability, and failure mode at the interface between lithium disilicate glass-ceramic and resin cement. The protocols compared were a self-etching ceramic primer and the conventional hydrofluoric acid (HF) etching followed by silane. Methods: Fifty lithium disilicate specimens were randomly divided into five surface treatment groups (n=10 each). A control group received no treatment. The remaining 4groups included: 5% HF etch with Monobond Plus thermocycled and non-thermocycled, Monobond Etch & Prime (MEP), thermocycled and non-thermocycled. Microshear bond strength (microSBS) was assessed before and after thermocycling to evaluate bond durability. Failure modes (adhesive, mixed, cohesive in resin/ceramic) were recorded under a stereomicroscope. Results: Both surface treatment protocols exhibited comparable microSBS for both pre- and post-thermocycling results. Moreover, bone durability obtained from the two treatment protocols seemed to be comparable. Most groups displayed adhesive/mixed failures. Notably, the self-etching ceramic primer group showed cohesive
📖 افتح في inklap 🔗 DOI 📮 اطلب بحثاً